Development of magnetic nanoparticles Fe+32 X+21O4 (X= Fe, Co y Ni) coated by amino silane

Authors

  • I A Flores Urquizo Universidad Autónoma de Ciudad Juárez, Instituto de Ingeniería y Tecnología
  • P García Casillas Universidad Autónoma de Ciudad Juárez, Instituto de Ingeniería y Tecnología
  • C Chapa González Universidad Autónoma de Ciudad Juárez, Instituto de Ingeniería y Tecnología

DOI:

https://doi.org/10.17488/RMIB.38.1.36

Keywords:

Magnetite, Nanomaterials, Hyperthermia

Abstract

Magnetic nanoparticles are proposed as heat mediators in hyperthermia treatments. In this work, three core-shell materials of different composition and magnetic anisotropy were developed to determine their properties as crystal size, saturation magnetization and their coating with organic molecules. The magnetic core of these materials was made by means of the coprecipitation reaction, following the stoichiometric ratio X+2Fe2+3O4 where X is Fe, Co or Ni for each material. From the X-ray diffraction patterns the crystal size of each material was determined, these were 10.39 nm, 7.27 nm y 3.86 nm. In addition, magnetization was 55.84 emu/g, 36.56 emu/g y 16.21 emu/g for magnetite, cobalt ferrite and nickel respectively. Each material was coated with aminosilane and by FTIR the vibrational modes of the C-N, N-H, C-H and Si-O bonds involved in the coating were identified.

Downloads

Download data is not yet available.

Published

2017-01-15

How to Cite

Flores Urquizo, I. A., García Casillas, P., & Chapa González, C. (2017). Development of magnetic nanoparticles Fe+32 X+21O4 (X= Fe, Co y Ni) coated by amino silane. Revista Mexicana De Ingenieria Biomedica, 38(1), 402–411. https://doi.org/10.17488/RMIB.38.1.36

Issue

Section

Special Issue

Share on:

Dimensions Citation